Method for forming metal wiring layer of semiconductor device

ABSTRACT

A method for forming a metal wiring layer in a semiconductor device using a dual damascene process is provided. A stopper layer, an interlayer insulating layer, and a hard mask layer are sequentially formed on a semiconductor substrate having a conductive layer. A first photoresist pattern that comprises a first opening having a first width is formed on the hard mask layer. The hard mask layer and portions of the interlayer insulating layer are etched using the first photoresist pattern as an etching mask, thereby forming a partial via hole having the first width. The first photoresist pattern is removed. An organic material layer is coated on the semiconductor substrate having the partial via hole is formed to fill the partial via hole with the organic material layer. A second photoresist pattern that comprises a second opening aligned with the partial via hole and having a second width greater than the first width is formed on the coated semiconductor substrate. The organic material layer and the hard mask layer on the interlayer insulating layer are etched using the second photoresist pattern as an etching mask. The second photoresist pattern and the organic material layer are simultaneously removed. A wiring region having the second width and a via hole having the first width are formed by etching the interlayer insulating layer using the hard mask layer as an etching mask.

CROSS-REFERENCE TO RELATED APPLICATION

[0001] This application claims priority to Korean Patent Application No. 2001-26966 filed on May 17, 2001.

BACKGROUND

[0002] 1. Technical Field

[0003] The present invention relates to a method for fabricating a semiconductor device, and more particularly, to a method for forming a metal wiring layer in a semiconductor device through a dual damascene process.

[0004] 2. Description of Related Art

[0005] As the integration density of semiconductor devices increases, a gap width between metal wiring layers in the semiconductor devices decreases. Consequently, it has been necessary to design metal wiring layers having a multi-layered wiring structure. However, parasitic resistance and capacitance existing between adjacent metal wiring layers in a lateral direction or in a vertical direction may effect the performance of the semiconductor devices.

[0006] Such parasitic resistance and capacitance components in a metal wiring layer generally cause a decrease in the operating speed, and thus deteriorate the electrical characteristics of the device. Further, the parasitic resistance and capacitance components increase the total power consumption of chips in the semiconductor device and an amount of signal leakage. Accordingly, a need exists to develop a method for forming a multi-layered wiring layer having low parasitic resistance and capacitance in a super-highly integrated semiconductor device.

[0007] Typically, a multi-layered wiring structure that has low parasitic resistance and capacitance is formed of a metal having low specific resistance or a dielectric layer having a low dielectric constant. For instance, a metal wiring layer that is formed of a material having low specific resistance such as copper has been studied. It is difficult to form a copper wiring layer by patterning copper using photolithography. Thus, a dual damascene process is commonly used to form such a copper wiring layer.

[0008]FIGS. 1 through 5 are cross-sectional views of a metal wiring layer in a semiconductor device formed according to a conventional method. Referring to FIG. 1, a stopper layer 104 is formed on a semiconductor substrate 100, on which a predetermined conductive layer 102 has been formed. An interlayer insulating layer 106 is formed on the stopper layer 104. Next, a first photoresist pattern 108 is formed on the interlayer insulating layer 106. The first photoresist pattern 108 comprises a first opening H₁ having a first width W₁ and partially exposing the surface of the interlayer insulating layer 106. In other words, the interlayer insulating layer 106 is covered with photoresist, and then the photoresist is exposed to light and developed, thereby forming the first photoresist pattern 108.

[0009] Referring to FIG. 2, the interlayer insulating layer 106 is etched using the first photoresist pattern 108 as an etching mask until the top surface of the stopper layer 104 is exposed. Thus, a via hole 110 having the first width W₁ is formed in an interlayer insulating layer 106 a. The first photoresist pattern 108 is removed by a conventional method such as an ashing process.

[0010] Referring to FIG. 3, a second photoresist pattern 112 is formed on the interlayer insulating layer 106 a having the via hole 110. The second photoresist pattern 112 comprises a second opening H₂ having a second width W₂ greater than the first width W₁ and partially exposing the surface of the interlayer insulating layer 106 a. The second opening H₂ is aligned with the via hole 110.

[0011] Referring to FIG. 4, the interlayer insulating layer 106 a is etched using the second photoresist pattern 112 as an etching mask by a dry etching method. As a result, a wiring region 114 having the second width W₂ is formed in an interlayer insulating layer 106 b, and a via hole 110 a having the first width W₁ is formed at the lower part of the wiring region 114 to connect the conductive layer 102 to the wiring region 114. However, during the etching process of the interlayer insulating layer 106 a, the stopper layer 104 may be etched with the interlayer insulating layer 106 a, thereby exposing the conductive layer 102.

[0012] Even though the interlayer insulating layer 106 b has a high etching selectivity to a stopper layer 104 a, the stopper layer 104 exposed through the via hole 110 (See FIG. 3) is inevitably etched at a predetermined speed during the etching of the interlayer insulating layer 106 a. Accordingly, after etching of the interlayer insulating layer 106 b is completed, the exposed stopper layer 104 may be completely etched, and thus the conductive layer may be exposed to an etching atmosphere. If the conductive layer 102, for example, a copper wiring layer, is exposed to an etching atmosphere, hard polymer (not shown) is formed along sidewalls of the interlayer insulating layer 106 b. Such hare polymer is difficult to remove. The hard polymer is more easily formed for a case where the interlayer insulating layer 106 a to be etched is deeper, the stopper layer 104 a is thinner, and the etching selectivity of the stopper layer 104 a with respect to the interlayer insulating layer 106 b is smaller.

[0013] Referring to FIG. 5, the second photoresist pattern 112 is removed by an ashing process. The ashing process uses an oxygen-based plasma. During the removal of the second photoresist pattern 112, that is, during the ashing process, the exposed conductive layer 102 may react with oxygen and form a metal oxide layer 116. The metal oxide layer 116 rapidly increases electrical resistance. Thus, even though the wiring region 114 and the via hole 110 a are filled with a conductive material, a metal wiring layer (not shown) and the conductive layer 102 cannot be electrically connected to each other, thus causing a lifting phenomenon. Further, since the ashing process using an oxygen-based plasma is performed after forming the wiring region 114 and the via hole 110 a, the process may damage to the surface of the interlayer insulating layer 106 b. For instance, H₂O, OH, CO₂, and H₂ released during the ashing process stick to the surface of the interlayer insulating layer 106 b, and thus the dielectric constant of the interlayer insulating layer 106 b may be rapidly increased.

[0014]FIGS. 6 through 10 are cross-sectional views of another metal wiring layer in a semiconductor device formed according to another conventional method. Referring to FIG. 6, a stopper layer 204 is formed on a semiconductor substrate, on which a conductive layer 202 has been formed. An interlayer insulating layer 206 is formed on the stopper layer 204. Next, a first photoresist pattern 208, which includes a first opening H₁ having a first width W₁ and partially exposing the surface of the interlayer insulating layer 206, is formed on the interlayer insulating layer 206. In other words, the interlayer insulating layer 206 is covered with photoresist, and then the photoresist is exposed to light and developed, thereby forming the first photoresist pattern 208.

[0015] Referring to FIG. 7, the interlayer insulating layer 206 is partially etched using the first photoresist pattern 208 as an etching mask so that a partial via hole 210 having the first width W₁ is formed in an interlayer insulating layer 206 a. The first photoresist pattern 208 is removed by a typical method such as an ashing process.

[0016] Referring to FIG. 8A, a second photoresist pattern 212 is formed on the interlayer insulating layer 206 a having the partial via hole 210. The second photoresist pattern 212 comprises a second opening H₂ having a second width W₂ greater than the first width W₁ and partially exposing the surface of the interlayer insulating layer 206 a. The second opening H₂ is formed to be aligned with the partial via hole 210. However, photoresist from the second photoresist pattern 212 may remain on the bottom surface of the partial via hole 210 during the forming of the second photoresist pattern 212 on the interlayer insulating layer 206 a. Since the remaining photoresist will act as a barrier to a subsequent etching process of the interlayer insulating layer 206 a, an unopened via hole may be formed after etching the interlayer insulating layer 206 a.

[0017]FIG. 8B illustrates an exemplary misaligned second photoresist pattern 212 a. In this case, photoresist may also remain on the bottom surface of the partial via hole 210 as shown in FIG. 8A.

[0018] Referring to FIG. 9a, the interlayer insulating layer 206 a is etched using the second photoresist pattern 212 as an etching mask by a dry etching method. As a result, a wiring region 214 having the second width W₂ is formed in the interlayer insulating layer 206 b, and a via hole 210 a having the first width W₁ is formed under the wiring region 214 so as to connect the conductive layer 202 to the wiring region 214. However, the photoresist remaining on the bottom surface of the partial via hole 210 of FIG. 8A acts as a barrier to the etching process of the interlayer insulating layer 206 a. Thus, the interlayer insulating layer 206 b positioned under the partial via hole 210 of FIG. 8A cannot be etched, and thus the via hole 210 a may not expose the conductive layer 202.

[0019]FIG. 9B illustrates the semiconductor substrate 200 on which the mis-aligned second photoresist pattern 212 a is formed. The wiring region 214 and the via hole 210 a are formed by etching the interlayer insulating layer 206 a using the misaligned second photoresist pattern 212 a as an etching mask. As shown in FIG. 9B, if a second photoresist pattern is misaligned, the width of the via hole 211a is less than the first width W₁, and the profile of the via hole 291 a is deteriorated. As described above with reference to FIG. 9A, if photoresist from the mis-aligned second photoresist pattern 212 a remains on the bottom surface of the partial via hole 210 (as shown in FIG. 9B), a via hole (not shown) that does not expose the conductive layer 202 may be formed.

[0020]FIG. 10A is illustrates an exemplary metal wiring layer having an unopened via hole. Referring to FIGS. 9A and 10A, the second photoresist pattern 212 is removed by an ashing process. At this time, the photoresist remaining on the bottom surface of the via hole 210 a of FIG. 9A is also removed. However, as described above, since the via hole 210 does not expose the conductive layer 202 because of the photoresist remaining on the bottom surface of the via hole 210 a of FIG. 9A, the via hole 210 a cannot connect the wiring region 214 to the conductive layer 202. Further, since the ashing process is performed using an oxygen-based plasma after forming the wiring region 214 and the via hole 210 a, the process may damage to the surface of the interlayer insulating layer 206 b. In other words, H₂O, OH, CO₂, and H₂ released during the ashing process may stick to the surface of the interlayer insulating layer 206 b, and thus the dielectric constant of the interlayer insulating layer 206 b may increase rapidly.

[0021]FIG. 10B illustrates the semiconductor substrate 200 after the misaligned second photoresist pattern 212 a is removed. As shown in FIG. 10B, the via hole 210 a having a width less than the first width W₁ is formed, thereby deteriorating the profile of the via hole 210 a. Further, when, as described above, photoresist from the mis-aligned second photoresist pattern 212 a remains on the bottom surface of the partial via hole 210 (as shown in FIG. 8B), an unopened via hole (not shown) is formed, thereby disconnecting the wiring region 214 and the conductive layer 202.

SUMMARY OF THE INVENTION

[0022] It is an object of the present invention to provide a method for forming a metal wiring layer in a semiconductor device that is capable of preventing a metal oxide layer from being generated on a conductive layer during the removal of a second photoresist pattern.

[0023] It is another object of the present invention to provide a method for forming a metal wiring layer in a semiconductor device that can prevent photoresist from remaining on the bottom surface of a partial via hole.

[0024] It is further object of the present invention to provide a method for forming a metal wiring layer in a semiconductor device that can prevent deterioration of the profile of a via hole even if misalignment of a second photoresist pattern.

[0025] According to one aspect of the present invention, a method is provided for forming a metal wiring layer of a semiconductor device. A stopper layer is formed on a semiconductor substrate having a conductive layer. An interlayer insulating layer is formed on the stopper layer. A hard mask layer is formed on the interlayer insulating layer. A first photoresist pattern that comprises a first opening having a first width and partially exposing the surface of the hard mask layer is formed on the hard mask layer. A partial via hole is formed by etching the hard mask layer and portions of the interlayer insulating layer using the first photoresist pattern as an etching mask. The first photoresist pattern is removed. The semiconductor substrate having the partial via hole is coated with an organic material layer to fill the partial via hole with the organic material layer. A second photoresist pattern that comprises a second opening having a second width and formed to be aligned with the partial via hole is formed on the coated semiconductor substrate. The organic material layer and the hard mask layer on the interlayer insulating layer are etched using the second photoresist pattern as an etching mask. At the same time, the second photoresist pattern and the organic material layer are removed. A wiring region having a second width and a via hole having the first width are formed by etching the interlayer insulating layer using the hard mask layer as an etching mask.

[0026] In another aspect of the present invention, the method further comprises the steps of removing the stopper layer exposed through the via hole, forming a barrier layer along the step difference of the semiconductor substrate, depositing a conductive material on the semiconductor substrate on which the barrier layer is formed and filling the wiring region and the via hole with the conductive material, and performing chemical mechanical polishing on the semiconductor substrate.

[0027] In a further aspect of the present invention, the portions of the interlayer insulating layer is etched to an etch depth that is substantially the same as the thickness of the interlayer insulating layer directly below the partial via hole.

[0028] Preferably, the conductive layer comprises a copper wiring layer.

[0029] Preferably, the stopper layer comprises one of a silicon nitride layer and a silicon carbide layer, having a high etching selectivity to the interlayer insulating layer.

[0030] Preferably, the interlayer insulating layer comprises a material layer having a high etching selectivity to the stopper layer and the hard mask layer and a low dielectric constant.

[0031] Preferably, the hard mask layer comprises one of a silicon nitride layer and a silicon carbide layer, having a high etching selectivity to the interlayer insulating layer.

[0032] Preferably, the organic material layer comprises a carbon-based bottom anti-reflection coating (BARC) layer.

[0033] Preferably, the organic material layer and the hard mask layer on the interlayer insulating layer is etched by using an etching gas comprising one of O₂ and both N₂ and H₂.

[0034] Preferably, the barrier layer comprises one of a Ta layer, a TaN layer, a Ti layer, a TiN layer, and a combination thereof.

[0035] According to another aspect of the present invention, a method is provided for forming a wiring layer of a semiconductor device according to a second embodiment of the present invention. A first stopper layer is formed on a semiconductor substrate having a conductive layer. A first interlayer insulating layer is formed on the first stopper layer. A second stopper layer is formed on the first interlayer insulating layer. A second interlayer insulating layer is formed on the second stopper layer. A hard mask layer is formed on the second interlayer insulating layer. A first photoresist pattern that comprises a first opening having a first width and partially exposing the surface of the hard mask layer is formed on the hard mask layer. A partial via hole having the first width is formed by etching the hard mask layer, the second interlayer insulating layer, and the second stopper layer using the first photoresist pattern as an etching mask. The first photoresist pattern is removed. The semiconductor substrate having the partial via hole is coated with an organic material layer to fill the partial via hole with the organic material layer. A second photoresist pattern that comprises a second opening aligned with the partial via hole and having a second width is formed on the coated semiconductor substrate. The organic material layer and the hard mask layer on the second interlayer insulating layer are etched using the second photoresist pattern as an etching mask. At the same time, the second photoresist pattern and the organic material layer are removed. A wiring region having the second width and a via hole having the first width in the second and first interlayer insulating layers are formed by etching the second and first interlayer insulating layers, respectively, using the hard mask layer as an etching mask.

[0036] According to still another aspect of the present invention, a method is provided for forming a wiring layer of a semiconductor device according to a third embodiment of the present invention. A stopper layer is formed on a semiconductor substrate, on which a conductive layer is formed. An interlayer insulating layer is formed on the stopper layer. A hard mask layer is formed on the interlayer insulating layer. A first photoresist pattern that comprises a first opening having a first width and partially exposing the surface of the hard mask is formed. A partial via hole having the first width is formed by etching the hard mask layer and portions of the interlayer insulating layer using the first photoresist pattern as an etching mask. The first photoresist pattern is removed. The semiconductor substrate having the partial via hole is formed is coated with a spin-on-glass (SOG) layer to fill the partial via hole with the SOG layer. A second photoresist pattern that comprises a second opening aligned with the partial via hole and having a second width is formed on the semiconductor substrate coated with the SOG layer. The SOG layer and the hard mask layer on the interlayer insulating layer are etched using the second photoresist pattern as an etching mask. The second photoresist pattern is removed. The SOG layer formed on the hard mask layer and in the partial via hole is wet-etched and removed. A wiring region having the second width and a via hole having the first width are formed by etching the interlayer insulating layer using the hard mask layer as an etching mask.

[0037] According to further aspect of the present invention, a method is provided for forming a wiring layer of a semiconductor device according to a fourth embodiment of the present invention. A first stopper layer is formed on a semiconductor substrate, on which a conductive layer is formed. A first interlayer insulating layer is formed on the first stopper layer. A second stopper layer is formed on the first interlayer insulating layer. A second interlayer insulating layer is formed on the second stopper. A hard mask layer is formed on the second interlayer insulating layer. A first photoresist pattern that comprises a first opening having a first width and partially exposing the surface of the hard mask layer is formed on the hard mask layer. A partial via hole having the first width is formed by etching the hard mask layer, the second interlayer insulating layer, and the second stopper layer using the first photoresist pattern as an etching mask. The first photoresist pattern is removed. The semiconductor substrate having the partial via hole is coated with a spin-on-glass (SOG) layer to fill the partial via hole with the SOG layer. A second photoresist pattern that comprises a second opening aligned with the partial via hole and having a second width is formed on the coated semiconductor substrate. The SOG layer and the hard mask layer on the second interlayer insulating layer are etched using the second photoresist pattern as an etching mask. The second photoresist pattern is removed. The SOG layer formed on the hard mask layer and in the partial via hole is wet-etched and removed. A wiring region having the second width and a via hole in the second and first interlayer insulating layers are formed by etching the second and first interlayer insulating layers, respectively, using the hard mask layer as an etching mask.

BRIEF DESCRIPTION OF THE DRAWINGS

[0038] The above objects and advantages of the present invention will become more apparent by describing in detail preferred embodiments thereof with reference to the attached drawings in which:

[0039]FIGS. 1 through 6 are cross-sectional views of a metal wiring layer in a semiconductor device formed according to a conventional method;

[0040]FIGS. 6 through 10B are cross-sectional views of another metal wiring layer in a semiconductor device formed according to another conventional method;

[0041]FIGS. 11 through 19 are cross-sectional views of a metal wiring layer in a semiconductor device illustrating a method for forming a metal wiring layer according to a first embodiment of the present invention;

[0042]FIGS. 20 through 26 are cross-sectional views of a metal wiring layer in a semiconductor device illustrating a method for forming a metal wiring layer according to a second embodiment of the present invention;

[0043]FIGS. 27 through 31 are cross-sectional views of a metal wiring layer in a semiconductor device illustrating a method for forming a metal wiring layer according to a third embodiment of the present invention; and

[0044]FIGS. 32 through 36 are cross-sectional views of a metal wiring layer in a semiconductor device illustrating a method for forming a metal wiring layer according to a fourth embodiment of the present invention.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

[0045] The present invention will now be described more fully with reference to the accompanying drawings, in which preferred embodiments of the invention are shown. The present invention may, however, be embodied in many different forms and should not be construed as being limited to the embodiments set forth herein. Rather, these embodiments are provided so that this disclosure will be thorough and complete, and will fully convey the concept of the invention to those skilled in the art. In the drawings, the thickness of layers and regions are exaggerated for clarity. It will also be understood that when a layer is referred to as being “on” another layer or substrate, it can be directly on the other layer or substrate, or intervening layers may also be present. Similar reference numerals denote elements having the same or similar functions, and thus their description will be omitted.

[0046]FIGS. 11 through 19 are cross-sectional views of a metal wiring layer in a semiconductor device illustrating a method for forming a metal wiring layer according to a first embodiment of the present invention. Referring to FIG. 11, a stopper layer 304 is formed on a semiconductor substrate 300, on which a predetermined conductive layer 302 has been formed. The conductive layer 302 comprises an impurity-doped region, a copper (Cu) wiring layer, or another metal wiring layer. The stopper layer 304 is preferably formed of a material having a high etching selectivity to an interlayer insulating layer 306 (which is formed on the stopper layer 304) such as a silicon nitride (Si₃N₄) layer or a silicon carbide (SiC) layer.

[0047] The interlayer insulating layer 306 is formed on the stopper layer 304. The interlayer insulating layer 306 preferably comprises a material having a low dielectric constant, for example, a SiOC layer, a porous SiO₂ layer, a phosphorous silicate glass (PSG) layer, a boron phosphorous silicate glass (BPSG) layer, an undoped silicate glass (USG) layer, a fluorine-doped silicate glass (FDSG) layer, a high-density plasma (HDP) layer, a plasma-enhanced tetraethylorthosilicate (PE-TEOS) layer, or a spin-on-glass (SOG) layer. Further, the interlayer insulating layer 306 preferably comprises a material having a high etching selectivity to the stopper layer 304.

[0048] A hard mask layer 308 is formed on the interlayer insulating layer 306. The hard mask layer 308 is preferably formed of a material having a high etching selectivity to the interlayer insulating layer 306 such as a silicon nitride layer or a silicon carbide layer.

[0049] A first photoresist pattern 310 is formed on the hard mask layer 308. The first photoresist pattern 310 comprises a first opening HI having a first width W₁ and partially exposing the surface of the hard mask layer 308. For instance, the hard mask layer 308 is covered with photoresist and then the photoresist is exposed to light and developed, thereby forming the first photoresist pattern 310.

[0050] Referring to FIG. 12, the hard mask layer 308 and portions of the interlayer 10 insulating layer 306 are etched using the first photoresist pattern 310 as an etching mask.

[0051] At this time, a predetermined thickness of an interlayer insulating layer 306 a is left without being etched. For instance, the depth to which the interlayer insulating layer 306 is etched, that is, the depth of a partial via hole 312, is substantially the same as the thickness of the interlayer insulating layer 306 a left after the etching process. Next, the first photoresist pattern 310 is removed by a typical method such as an ashing process.

[0052] Referring to FIG. 13, an organic material layer 314 is formed on the semiconductor substrate 300, in which the partial via hole 312 has been formed, so as to fill the partial via hole 312 with the organic material layer 314. The organic material layer 314 may be formed only in the partial via hole 312 or may also be thinly formed on a hard mask layer 308 a. The organic material layer 314 preferably comprises a carbon-based organic material, for example, a bottom anti-reflection coating (BARC) layer. The organic material layer 314 may be formed by a spin coating method, in which case the spin coater spins at about 1000-1500 rpm. After coating the semiconductor substrate 300 with the organic material layer 314, the semiconductor substrate 300 is baked at a temperature between 100° C. and 150° C.

[0053] Referring to FIG. 14, a second photoresist pattern 316 is formed on the semiconductor substrate 300 having the organic material layer 314. The second photoresist pattern 316 comprises a second opening H₂ having a second width W₂ greater than the first width W₁ and partially exposing the organic material layer 314. The second opening H₂ is formed to be aligned with the partial via hole 312 and to be positioned on the partial via hole 312.

[0054] Referring to FIG. 15, the organic material layer 314 and the hard mask layer 308 a on the interlayer insulating layer 306 a are dry-etched using the second photoresist pattern 316 as an etching mask. At this time, an etching gas comprises one of oxygen (O₂) and both N₂ and H₂. Further, the etching gas may comprise one of a C_(x)F_(y)-based gas, a C_(x)H_(y)F_(z)-based gas, an inert gas, such as Ar, and a gas comprising CO or O₂. The organic material layer 314 in the partial via hole 312 is recessed to a predetermined depth due to the process for etching the organic material layer 314 and the hard mask layer 308 a.

[0055] Referring to FIG. 16, the second photoresist pattern 316 is removed. The second photoresist pattern 316 may be removed by a typical method such as an ashing process. At this time, the organic material layer 314 is removed along with the second photoresist pattern 316. In other words, the organic material existing on the hard mask layer 308 a and in the partial via hole 312 is removed in the process for removing the second photoresist pattern 316. After the second photoresist pattern 316 and the organic material layer 314 are removed, a hard mask layer 308 b having an opening with the second width W₂ is exposed.

[0056] Referring to FIG. 17, the interlayer insulating layer 306 a is dry-etched using the hard mask layer 308 b as an etching mask, thereby simultaneously formning a wiring region 318 and a via hole 312 a. In other words, the wiring region 318 having the second width W₂ is formed in the interlayer insulating layer 306 b, and the via hole 312 a having the first width W₁ less than the second width W₂ is formed under the wiring region 318. Since the hard mask layer 308 b is used as an etching mask, the hard mask layer 308 b has a sufficient thickness to endure the process for etching the interlayer insulating layer 306 a.

[0057] Next, the stopper layer 304 exposed through the via hole 312 a is etched and removed. At this time, the hard mask layer 308 b may be etched and removed along with the stopper layer 304 exposed through the via hole 312 a or may be left. For instance, the hard mask layer 308 b, in FIG. 17, is left on the interlayer insulating layer 306 a.

[0058] Referring to FIG. 18, a barrier layer 320 is formed along the step difference of the semiconductor substrate 300 after the stopper layer 304 is removed. The barrier layer 320 preferably comprises one of a Ta layer, a TaN layer, a Ti layer, a TiN layer, and a combination thereof.

[0059] Referring to FIG. 19, a conductive material is deposited to fill the wiring region 318 and the via hole 312 a. Next, the semiconductor substrate 300 is planarized by chemical mechanical polishing. At this time, the barrier layer 320 on the hard mask layer 308 b is removed by chemical vapor polishing. Through the planarization process, a metal wiring layer 322 is formed in the wiring region 318, and a via contact 324 connecting the conductive layer 302 to the metal wiring layer 322 is formed in the via hole 312 a. The hard mask layer 308 b may be removed by chemical mechanical polishing which is performed until the interlayer insulating layer 306 b is exposed. Alternatively, the hard mask layer 308 b may be left.

[0060]FIGS. 20 through 26 are cross-sectional views of a metal wiring layer in a semiconductor device illustrating a method for forming a metal wiring layer according to a second embodiment of the present invention. Referring to FIG. 20, a first stopper layer 404 is formed on a semiconductor substrate 400, on which a predetermined conductive layer 402 has been formed. The conductive layer 402 may comprise an impurity-doped region, a copper (Cu) wiring layer, or another metal wiring layer formed on the semiconductor substrate 400. The first stopper layer 404 preferably comprises a material having a high etching selectivity to a first interlayer insulating layer 405 (which is to be formed on the first stopper layer 404) such as a silicon nitride (Si₃N₄) layer or a silicon carbamide (SiC) layer.

[0061] The first interlayer insulating layer 405 is formed on the first stopper layer 404. The first interlayer insulating layer 405 preferably comprises a material having a low dielectric constant, for example, a SiOC layer, a porous SiO₂ layer, a phosphorous silicate glass (PSG) layer, a boron phosphorous silicate glass (BPSG) layer, an undoped silicate glass (USG) layer, a fluorine-doped silicate glass (FDSG) layer, a high-density plasma (HDP) layer, a plasma-enhanced tetraethylorthosilicate (PE-TEOS) layer, or a spin-on-glass (SOG) layer. Further, the first interlayer insulating layer 405 preferably comprises a material having a high etching selectivity to the first stopper layer 404.

[0062] A second stopper layer 406 is formed on the first interlayer insulating layer 405. The second stopper layer 406 preferably comprises a material having a high etching selectivity to a second interlayer insulating layer 407 (which is to be formed on the second stopper layer 406) such as a silicon nitride (Si₃N₄) layer or a silicon carbamide (SiC) layer.

[0063] The second interlayer insulating layer 407 is preferably comprises a material having a low dielectric constant such as a SiOC layer, a porous SiO₂ layer, a phosphorous silicate glass (PSG) layer, a boron phosphorous silicate glass (BPSG) layer, an undoped silicate glass (USG) layer, a fluorine-doped silicate glass (FDSG) layer, a high-density plasma (HDP) layer, a plasma-enhanced tetraethylorthosilicate (PE-TEOS) layer, or a spin-on-glass (SOG) layer. Further, the second interlayer insulating layer 407 preferably comprises a material having a high etching selectivity to the second stopper layer 406. The second interlayer insulating layer 407 may be formed of a different material from the material of the first interlayer insulating layer 405 or may be formed of the same material as the first interlayer insulating layer 405. For example, the second interlayer insulating layer 407, in FIG. 20, is preferably formed of the same material as the first interlayer insulating layer 405.

[0064] A hard mask layer 408 is formed on the second interlayer insulating layer 407. The hard mask layer 408 preferably comprises a material having a high etching selectivity to the second interlayer insulating layer 407 such as a silicon nitride (Si₃N₄) layer or a silicon carbide (SiC) layer.

[0065] A first photoresist pattern 410 is formed on the hard mask layer 408. The first photoresist pattern 410 comprises a first opening H₁ having a first width W₁ and partially exposing the surface of the hard mask layer 408. In other words, photoresist is formed on the hard mask layer 408 and then is exposed to light and developed, thereby forming the first photoresist pattern 410.

[0066] Referring to FIG. 21, the hard mask layer 408, the second interlayer insulating layer 407, and the second stopper layer 406 are etched using the first photoresist pattern 410 as an etching mask, thereby forming a partial via hole 412 having the first width W₁ on a second interlayer insulating layer 407 a. Next, the first photoresist pattern 410 is removed. The first photoresist pattern 410 may be removed by a typical method such as an ashing process.

[0067] Referring to FIG. 22, an organic material layer 414 is formed on the semiconductor substrate 400, on which the partial via hole 412 has been formed, so as to fill the partial via hole 412 with the organic material layer 414. The organic material layer 414 may be formed in only the partial via hole 412 or may also be thinly formed on a hard mask layer 408 a. The organic material layer 414 preferably comprises a carbon-based organic material, for example, a bottom anti-reflection coating (BARC) layer. The organic material layer 414 may be formed by spin coating, in which case a spin coater spins at about 1000-5000 rpm. After coating the semiconductor substrate 400 with the organic material layer 414, the semiconductor substrate 400 is baked at a temperature between 100° C. and 150° C.

[0068] Referring to FIG. 23, a second photoresist pattern 416 is formed on the semiconductor substrate 400, on which the organic material layer 414 has been formed. The second photoresist pattern 416 comprises a second opening H₂ having the second width W₂ greater than the first width W₁, and partially exposing the organic material layer 414. The second opening H₂ is formed to be aligned with the partial via hole 412 and to be positioned on the partial via hole 412.

[0069] Referring to FIG. 24, the organic material layer 414 and the hard mask layer 408 a on a second interlayer insulating layer 407 a are dry-etched using the second photoresist pattern 416 as an etching mask. At this time, an etching gas comprises one of a gas comprising oxygen (O₂) and a gas comprising N₂ and H₂. Alternatively, the etching gas may comprise one of a C_(x)F_(y)-based gas, a C_(x)H_(y)F_(z)-based gas, an inert gas, such as Ar, and a gas comprising CO or O₂. The organic material layer 414 in the partial via hole 412 is recessed to a predetermined depth due to the process for etching the organic material layer 414 and the hard mask layer 408 a.

[0070] Referring to FIG. 25, the second photoresist pattern 416 is removed. The second photoresist pattern 416 may be removed by a typical method such as an ashing process. At this time, the organic material layer 414 is removed along with the second photoresist pattern 416. In other words, the organic material layer 414 existing on the hard mask layer 408 b or in the partial via hole 412 is removed in the process for removing the second photoresist pattern 416. After the second photoresist pattern 416 and the organic material layer 414 are removed, the hard mask layer 408 b having an opening with the second width W₂ is exposed.

[0071] Referring to FIG. 26, the second interlayer insulating layer 407 a and the first interlayer insulating layer 405 are dry-etched using the hard mask layer 408 b as an etching mask, thereby simultaneously forming a wiring region 418 and a via hole 412 a. In other words, the wiring region 418 having the second width W₂ is formed in a second interlayer insulating layer 407 b, and the via hole 412 a having the first width W₁ less than the second width W₂ is formed in the first interlayer insulating layer 405 a.

[0072] Next, the first stopper layer 404 exposed by the via hole 412 a is etched and removed. A hard mask layer 408 b may be etched and removed along with the first stopper layer 404 exposed by the via hole 412 a, or it may be left. Subsequent processes are the same as those of the first embodiment of the present invention.

[0073]FIGS. 27 through 31 are cross-sectional views of a metal wiring layer in a semiconductor device illustrating a method for forming a metal wiring layer according to a third embodiment of the present invention. Referring to FIG. 27, a stopper layer 504, an interlayer insulating layer 506, and a hard mask layer 508 are sequentially formed on a semiconductor substrate 500, on which a predetermined conductive layer 502 has been formed. Next, a first photoresist pattern (not shown) that comprises an opening having a first width W₁ and partially exposing the surface of the hard mask layer 508 is formed on the semiconductor device. A partial via hole 512 is formed by etching the hard mask layer 508 and portions of the interlayer insulating layer 506 using the first photoresist pattern as an etching mask. The first photoresist pattern is removed. The above-described steps are the same as the corresponding steps of the first embodiment of the present invention. Here, the interlayer insulating layer 506 preferably comprises a material having a low dielectric constant such as a SiOC layer.

[0074] A spin-on-glass (SOG) layer 514 is formed on the semiconductor substrate 500, on which the partial via hole 512 has been formed, by spin coating. After coating the semiconductor substrate 500 with the SOG layer 514, the semiconductor substrate 500 is preferably baked at a temperature of 250-350° C. for about 30 seconds ˜5 minutes. The SOG layer 514 preferably comprises a material having high wet-etching selectivity to the interlayer insulating layer 506 a such as a hydro silsesquioxane (HSQ) layer or a SiO₂ layer. For example, the SOG layer 514 such as a HSG layer is rapidly etched in a HF solution, while the interlayer insulating layer 506 a such as a SiOC layer is hardly etched in the HF solution. For example, if a HSQ layer, a SiOC layer, and a SiC layer are wet-etched in a HF aqueous solution for 90 seconds (in which HF is diluted with water to a ratio of 1:500), the HSQ layer is etched to a thickness of 470 Å, the SiOC layer is etched to a thickness of 15-31 Å, and the SiC layer is etched to a thickness of 13 Å.

[0075] Referring to FIG. 28, a second photoresist pattern 516 is formed on the SOG layer 514. The second photoresist pattern 516 comprises a second opening H₂ having a second width W₂ greater than the first width W₁ and partially exposing the SOG layer 514. The second opening H₂ is formed to be aligned with the partial via hole 512. When the SOG layer 514 and the hard mask layer 508 a are etched using the second photoresist pattern 516 as an etching mask, the partial via hole 514 formed in the interlayer insulating layer 506 a is exposed.

[0076] Referring to FIG. 29, the SOG layer 514 and the hard mask layer 508 a on the interlayer insulating layer 506 a are dry-etched using the second photoresist pattern 516 as an etching mask. At this time, an etching gas may comprise one of a C_(x)F_(y)-based gas, a C_(x)H_(y)F_(z)-based gas, an inert gas, such as Ar, and a gas comprising CO, CO₂ or O₂. The dry etching is preferably performed at a pressure of 5-50 mTorr with a power of 1000˜5000 W for about 1˜2 minutes. During the dry etching, the SOG layer 514 filling the partial via hole 512 is recessed to a predetermined depth. The SOG layer 514 may be completely removed depending on etching conditions.

[0077] Referring to FIG. 30, the second photoresist pattern 516 is removed. The second photoresist pattern 516 may be removed by a typical method, such as an ashing process.

[0078] A SOG layer 514 a formed on the hard mask layer 508 b and in the partial via hole 512 is wet-etched and removed. At this time, an etching solution, for example, HF solution, preferably etches the SOG layer 514 a faster than the interlayer insulating layer 506 a, thereby removing only the SOG layer 514 a. For example, the SOG layer 514 a such as a HSQ layer is etched very fast in a HF solution, whereas the interlayer insulating layer 506 a such as a SiOC layer is hardly etched in the HF solution. For example, if a HSQ layer, a SiOC layer, and a SiC layer are wet-etched in a HF solution for 90 seconds (in which HF is diluted with water to a ratio of 1:500), the HSQ layer is etched to a thickness of 470 Å, the SiOC layer is etched to a thickness of 15-31 Å, and the SiC layer is etched to a thickness of 13 Å.

[0079] When the second photoresist pattern 516 and the SOG layer 514 a are removed, the hard mask layer 508 b, in which an opening having the second width W₂ is formed, is exposed.

[0080] Referring to FIG. 31, subsequent processes are the same as those of the first embodiment of the present invention. In other words, a process for simultaneously forming a wiring region 518 and a via hole 512 a by dry-etching the interlayer insulating layer 506 a using the hard mask layer 508 b as an etching mask and the subsequent processes are the same as those of the first embodiment of the present invention.

[0081]FIGS. 32 through 36 are cross-sectional views of a metal wiring layer in a semiconductor device illustrating a method for forming a metal wiring layer according to a fourth embodiment of the present invention. Referring to FIG. 32, a first stopper layer 604, a first interlayer insulating layer 605, a second stopper layer 606, a second interlayer insulating layer 607, and a hard mask layer 608 are sequentially formed on a semiconductor substrate 600, on which a predetermined conductive layer 602 has been formed. A first photoresist pattern (not shown) that comprises an opening having a first width W₁ and partially exposing the surface of the hard mask layer 608 is formed on the semiconductor substrate 600. The hard mask layer 608, the second interlayer insulating layer 607, and the second stopper layer 606 are etched using the first photoresist pattern (not shown) as an etching mask, thereby forming a partial via hole 612. The first photoresist pattern is removed. The above-described steps are the same as the corresponding steps of the second embodiment of the present invention.

[0082] Here, the second interlayer insulating layer 607 preferably comprises a SiOC layer having a low dielectric constant and a high etching selectivity to the hard mask layer 608 and the second stopper layer 606. The first interlayer insulating layer 605 preferably comprises a material having a low dielectric constant and having a high etching selectivity to the first stopper 604 layer such as a SiOC layer, a porous SiO₂ layer, a phosphorous silicate glass (PSG) layer, a boron phosphorous silicate glass (BPSG) layer, an undoped silicate glass (USG) layer, a fluorine-doped silicate glass (FDSG) layer, a high-density plasma (HDP) layer, a plasma-enhanced tetraethylorthosilicate (PE-TEOS) layer, or a spin-on-glass (SOG) layer. The second interlayer insulating layer 607 may be formed of a different material from the material of the first interlayer insulating layer 605. The second interlayer insulating layer 607, in FIG. 32, is preferably formed of the same material as the first interlayer insulating layer 605.

[0083] Next, a SOG layer 614 is formed on the semiconductor substrate 600 having the partial via hole 612 by spin coating. After coating the semiconductor substrate 600 with the SOG layer 614, the semiconductor substrate 600 is preferably baked at a temperature between 250° C. and 350° C. for about 30 seconds˜about 5 minutes. The SOG layer 614 preferably comprises a material layer having a high wet-etching selectivity to a second interlayer insulating layer 607 a such as a HSQ layer or a SiO₂ layer. For instance, the SOG layer such as a HSQ layer is etched very rapidly in a HF solution, whereas the second interlayer insulating layer 607 a such as a SiOC layer is hardly be etched in the HF solution. For example, if a HSQ layer, a SiOC layer, and a SiC layer are wet-etched in a HF aqueous solution for 90 seconds (in which HF is diluted with water to a ratio of 1:500), the HSQ layer is etched to a thickness of 470 Å, the SiOC layer is etched to a thickness of 15-31 Å, and the SiC layer is etched to a thickness of 13 Å.

[0084] Referring to FIG. 33, a second photoresist pattern 616 is formed on the SOG layer 614. The second photoresist pattern 616 comprises a second opening H₂ having a second width W₂ greater than the first width W₁, and partially exposing the SOG layer 614. The second opening H₂ is formed to be aligned with the partial via hole 712. When the SOG layer 614 and a hard mask layer 608 a are etched, the partial via hole 612 formed in the second interlayer insulating layer 607 a is exposed.

[0085] Referring to FIG. 34, the SOG layer 614 and the hard mask layer 608 a on the second interlayer insulating layer 607 a are dry-etched using the second photoresist pattern 616 as an etching mask. At this time, an etching gas may comprise one of a C_(x)F_(y)-based gas, a C_(x)H_(y)F_(z)-based gas, an inert gas, such as Ar, and a gas comprising CO, CO₂ or O₂. The dry etching is preferably performed at a pressure of about 5˜50 mTorr with a power of about 1000˜5000 W for about 1˜2 minutes. Due to the dry etching, the SOG layer 614 filling the partial via hole 612 is recessed to a predetermined depth. The SOG layer 614 may be completely removed depending on etching conditions.

[0086] Referring to FIG. 35, the second photoresist pattern 616 is removed. The second photoresist pattern 616 may be removed by a typical method such as an ashing process.

[0087] Next, a SOG layer 614 a formed on the hard mask layer 608 b and in the partial via hole 612 is wet-etched and removed. At this time, an etching solution, for example, a HF solution, preferably etches the SOG layer 614 a faster than the second interlayer insulating layer 607 a and thus selectively removes only the SOG layer 614 a. The SOG layer 614 a such as a HSQ layer is etched very fast in a HF solution, whereas the interlayer insulating layer 606 a such as a SiOC layer is hardly be etched in the HF solution. For example, if a HSQ layer, a SiOC layer, and a SiC layer are wet-etched in a HF aqueous solution for about 90 seconds (in which HF is diluted with water to a ratio of 1:500), the HSQ layer is etched to a thickness of 470 Å, the SiOC layer is etched to a thickness of 15-31 Å, and the SiC layer is etched to a thickness of 13 Å.

[0088] When the second photoresist pattern 616 and the SOG layer 614 a are removed, the hard mask layer 608 b, in which an opening having the second width W₂ is formed, is exposed.

[0089] Referring to FIG. 36, the second interlayer insulating layer 607 a and the first interlayer insulating layer 605 are dry-etched using the hard mask layer 608 b as an etching mask, thereby simultaneously forming a wiring region 618 and a via hole 612 a. In other words, the wiring region having the second width W₂ is formed in a second interlayer insulating layer 607 b, and the via hole 612 a having the first width W₁ less than the second width W₂ is formed in a first interlayer insulating layer 605 a.

[0090] Next, the first stopper layer 604 exposed by the via hole 612 a is etched and removed. At this time, the hard mask layer 608 b may be etched and removed along with the first stopper layer 604 exposed by the via hole 612 a or may be left. Subsequent processes are the same as those of the first embodiment of the present invention.

[0091] According to an embodiment of the present invention, a conductive layer is not exposed to an outside during the forming a wiring region and a via hole by etching an interlayer insulating layer (or second and first interlayer insulating layers). Thus, the embodiment of the present invention can prevent a metal oxide layer from being formed on a conductive layer during the removal of a second photoresist pattern. Further, since a partial via hole, in an embodiment of the present invention, is filled with an organic or an inorganic material before forming a second photoresist pattern, the remaining of photoresist on the bottom surface of the partial via hole can be prevented. Thus, a problem that a via hole expose a conductive layer never occurs. Furthermore, because of the filling organic or inorganic material in the partial via hole, deterioration of the profile of the via hole can be prevented even if misalignment of the second photoresist pattern. Further, since a wiring region and a via hole, in an embodiment of the present invention, are formed by an etch method using a hard mask layer as an etching mask, a surface of an interlayer insulating layer can be protected during the etching process.

[0092] While this invention has been particularly shown and described with reference to preferred embodiments thereof, it will be understood by those skilled in the art that various changes in form and details may be made therein without departing from the spirit and scope of the invention as defined by the appended claims. 

What is claimed is:
 1. A method for forming a metal wiring layer in a semiconductor device, comprising the steps of: forming a stopper layer on a semiconductor substrate, on which a conductive layer is formed; forming an interlayer insulating layer on the stopper layer; forming a hard mask layer on the interlayer insulating layer; forming a first photoresist pattern on the hard mask layer, wherein the first photoresist comprises a first opening having a first width and partially exposing the surface of the hard mask layer; forming a partial via hole by etching the hard mask layer and portions of the interlayer insulating layer using the first photoresist pattern as an etching mask; removing the first photoresist pattern; coating the semiconductor substrate comprising the partial via hole with an organic material layer to fill the partial via hole with the organic material layer; forming a second photoresist pattern on the coated semiconductor substrate, wherein the second photoresist pattern comprises a second opening having a second width greater than the first width and being formed to be aligned with the partial via hole; etching the organic material layer and the hard mask layer on the interlayer insulating layer using the second photoresist pattern as an etching mask; simultaneously removing the second photoresist pattern and the organic material layer; and forming a wiring region having the second width and a via hole having the first width by etching the interlayer insulating layer using the hard mask layer as an etching mask.
 2. The method of claim 1, wherein the step of etching portions of the interlayer insulating layer using the first photoresist pattern as an etching mask comprises the step of etching the interlayer insulating layer to an etch depth that is substantially the same as the thickness of the interlayer insulating layer directly below the partial via hole.
 3. The method of claim 1, wherein the conductive layer comprises a copper wiring layer.
 4. The method of claim 1, wherein the stopper layer comprises one of a silicon nitride layer and a silicon carbide layer, having a high etching selectivity to the interlayer insulating layer.
 5. The method of claim 1, wherein the interlayer insulating layer comprises a material layer having a high etching selectivity to the stopper layer and the hard mask layer and a low dielectric constant.
 6. The method of claim 5, wherein the interlayer insulating layer comprises one of a SiOC layer, a porous SiO₂ layer, a phosphorous silicate glass (PSG) layer, a boron phosphorous silicate glass (BPSG) layer, an undoped silicate glass (USG) layer, a fluorine-doped silicate glass (FDSG) layer, a high-density plasma (HDP) layer, a plasma-enhanced tetraethylorthosilicate (PE-TEOS) layer, and a spin-on-glass (SOG) layer.
 7. The method of claim 1, wherein the hard mask layer comprises one of a silicon nitride layer and a silicon carbide layer, having has a high etching selectivity to the interlayer insulating layer.
 8. The method of claim 1, wherein the organic material layer comprises a carbon-based bottom anti-reflection coating (BARC) layer.
 9. The method of claim 1, wherein the step of etching the organic material layer and the hard mask layer on the interlayer insulating layer using the second photoresist pattern as an etching mask is performed using an etching gas comprising one of O₂ and both N₂ and H₂.
 10. The method of claim 1, wherein the step of etching the organic material layer and the hard mask layer on the interlayer insulating layer using the second photoresist pattern as an etching mask is performed using an etching gas comprising one of a C_(x)F_(y)-based gas, a C_(x)H_(y)F_(z)-based gas, an inert gas, CO and O₂.
 11. The method of claim 1, further comprising the steps of: removing the stopper layer exposed through the via hole; forming a barrier layer along the step difference of the semiconductor substrate; depositing a conductive material on the semiconductor substrate on which the barrier layer is formed and filling the wiring region and the via hole with the conductive material; and performing chemical mechanical polishing on the semiconductor substrate.
 12. The method of claim 11, wherein the barrier layer comprises one of a Ta layer, a TaN layer, a Ti layer, a TiN layer, and a combination thereof.
 13. A method for forming a metal wiring layer in a semiconductor device, comprising the steps of: forming a first stopper layer on a semiconductor substrate, on which a conductive layer is formed; forming a first interlayer insulating layer on the first stopper layer; forming a second stopper layer on the first interlayer insulating layer; forming a second interlayer insulating layer on the second stopper layer; forming a hard mask layer on the second interlayer insulating layer; forming a first photoresist pattern on the hard mask layer, wherein the first photoresist pattern comprises a first opening having a first width and partially exposing the surface of the hard mask layer; forming a partial via hole having the first width by etching the hard mask layer, the second interlayer insulating layer, and the second stopper layer using the first photoresist pattern as an etching mask; removing the first photoresist pattern; coating the semiconductor substrate comprising the partial via hole with an organic material layer to fill the partial via hole with the organic material layer; forming a second photoresist pattern on the coated semiconductor substrate, wherein the second photoresist pattern comprises a second opening aligned with the partial via hole and having a second width greater than the first width; etching the organic material layer and the hard mask layer on the second interlayer insulating layer using the second photoresist pattern as an etching mask; simultaneously removing the second photoresist pattern and the organic material layer; and forming a wiring region having the second width and a via hole having the first width in the second and first interlayer insulating layers by etching the second and first interlayer insulating layers, respectively, using the hard mask layer as an etching mask.
 14. The method of claim 13, wherein the conductive layer comprises a copper wiring layer.
 15. The method of claim 13, wherein the first stopper comprises one of a silicon nitride layer and a silicon carbide layer, having a high etching selectivity to the first interlayer insulating layer.
 16. The method of claim 13, wherein the second stopper layer comprises one of a silicon nitride layer and a silicon carbide layer, having a high etching selectivity to the second interlayer insulating layer.
 17. The method of claim 13, wherein the first interlayer insulating layer is formed of a material having a high etching selectivity to the first stopper layer and the hard mask layer and a low dielectric constant.
 18. The method of claim 17, wherein the first interlayer insulating layer comprises one of a SiOC layer, a porous SiO₂ layer, a phosphorous silicate glass (PSG) layer, a boron phosphorous silicate glass (BPSG) layer, an undoped silicate glass (USG) layer, a fluorine-doped silicate glass (FDSG) layer, a high-density plasma (HDP) layer, a plasma-enhanced-tetraethylorthosilicate (PE-TEOS) layer, and a spin-on-glass (SOG) layer.
 19. The method of claim 13, wherein the second interlayer insulating layer is formed of a material having a high etching selectivity to the second stopper layer and the hard mask layer and a low dielectric constant.
 20. The method of claim 19, wherein the second interlayer insulating layer comprises one of a SiOC layer, a porous SiO₂ layer, a phosphorous silicate glass (PSG) layer, a boron phosphorous silicate glass (BPSG) layer, an undoped silicate glass (USG) layer, a fluorine-doped silicate glass (FDSG) layer, a high-density plasma (HDP) layer, a plasma-enhanced tetraethylorthosilicate (PE-TEOS) layer, and a spin-on-glass (SOG) layer.
 21. The method of claim 13, wherein the second interlayer insulating layer is formed of the same material as the first interlayer insulating layer.
 22. The method of claim 13, wherein the hard mask layer comprises one of a silicon nitride layer and a silicon carbide layer, having a high etching selectivity to the second interlayer insulating layer and the first interlayer insulating layer.
 23. The method of claim 13, wherein the organic material layer comprises a carbon-based bottom anti-reflection coating (BARC) layer.
 24. The method of claim 13, wherein the step of etching the organic material layer and the hard mask layer on the second interlayer insulating layer using the second photoresist pattern as an etching mask is performed using an etching gas comprising one of O₂ and both N₂ and H₂.
 25. The method of claim 13, wherein the step of etching the organic material layer and the hard mask layer on the second interlayer insulating layer using the second photoresist pattern as an etching mask is performed using an etching gas comprising one of a C_(x)F_(y)-based gas, a C_(x)H_(y)F_(z)-based gas, an inert gas, CO and O₂.
 26. The method of claim 13, further comprising the steps of; removing the stopper layer exposed through the via hole; forming a barrier layer along the step difference of the semiconductor substrate; depositing a conductive material on the semiconductor substrate on which the barrier layer is formed and filling the wiring region and the via hole with the conductive material; and performing chemical mechanical polishing on the semiconductor substrate.
 27. The method of claim 13, wherein the barrier layer comprises one of a Ta layer, a TaN layer, a Ti layer, a TiN layer, and a combination thereof.
 28. A method for forming a metal wiring layer in a semiconductor device, comprising the steps of: forming a stopper layer on a semiconductor substrate, on which a conductive layer is formed; forming an interlayer insulating layer on the stopper layer; forming a hard mask layer on the interlayer insulating layer; forming a first photoresist pattern on the semiconductor substrate, wherein the first photoresist pattern comprises a first opening having a first width and partially exposing the surface of the hard mask; forming a partial via hole having the first width by etching the hard mask layer and portions of the interlayer insulating layer using the first photoresist pattern as an etching mask; removing the first photoresist pattern; coating the semiconductor substrate comprising the partial via hole with a spin-on-glass (SOG) layer to fill the partial via hole with the SOG layer; forming a second photoresist pattern on the semiconductor substrate coated with the SOG layer, wherein the second photoresist pattern comprises a second opening aligned with the partial via hole and having a second width greater than the first width; etching the SOG layer and the hard mask layer on the interlayer insulating layer using the second photoresist pattern as an etching mask; removing the second photoresist pattern; wet-etching and removing the SOG layer formed on the hard mask layer and in the partial via hole; and forming a wiring region having the second width and a via hole having the first width by etching the interlayer insulating layer using the hard mask layer as an etching mask.
 29. The method of claim 28, wherein the step of etching portions of the interlayer insulating layer using the first photoresist pattern as an etching mask comprises the step of etching the interlayer insulating layer to an etch depth that is substantially the same as the thickness of the interlayer insulating layer directly below the partial via hole.
 30. The method of claim 28, wherein the conductive layer comprises a copper wiring layer.
 31. The method of claim 28, wherein the stopper layer comprises one of a silicon nitride layer and a silicon carbide layer, having an etching selectivity to the interlayer insulating layer.
 32. The method of claim 28, wherein the interlayer insulating layer comprises a material layer having a high etching selectivity to the stopper layer and the hard mask layer and a low dielectric constant.
 33. The method of claim 32, wherein the interlayer insulating layer comprises a SiOC layer.
 34. The method of claim 28, wherein the hard mask layer comprises one of a silicon nitride layer and a silicon carbide layer, having a high etching selectivity to the interlayer insulating layer and a low dielectric constant.
 35. The method of claim 28, wherein the SOG layer comprises one of a HSQ layer and a SiO₂ layer, having a high etching selectivity to the interlayer insulating layer.
 36. The method of claim 28, wherein the step of etching the SOG layer is performed using a HF solution as an etching gas, wherein the HF solution etches only the SOG layer.
 37. The method of claim 28, wherein the step of etching the organic material layer and the hard mask layer on the second interlayer insulating layer using the second photoresist pattern as an etching mask is performed using an etching gas comprising one of a C_(x)F_(y)-based gas, a C_(x)H_(y)F_(z)-based gas, an inert gas, CO and O₂.
 38. The method of claim 28, further comprising the steps of: removing the stopper layer exposed through the via hole; forming a barrier layer along the step difference of the semiconductor substrate; depositing a conductive material on the semiconductor substrate on which the barrier layer is formed and filling the wiring region and the via hole with the conductive material; and performing chemical mechanical polishing on the semiconductor substrate.
 39. The method of claim 38, wherein the barrier layer comprises one of a Ta layer, a TaN layer, a Ti layer, a TiN layer, and a combination thereof.
 40. A method for forming a wiring layer in a semiconductor device, comprising the steps of: forming a first stopper layer on a semiconductor substrate, on which a conductive layer is formed; forming a first interlayer insulating layer on the first stopper layer; forming a second stopper layer on the first interlayer insulating layer; forming a second interlayer insulating layer on the second stopper; forming a hard mask layer on the second interlayer insulating layer; forming a first photoresist pattern on the hard mask layer, wherein the first photoresist pattern comprises a first opening having a first width and partially exposing the surface of the hard mask layer; forming a partial via hole having the first width by etching the hard mask layer, the second interlayer insulating layer, and the second stopper layer using the first photoresist pattern as an etching mask; removing the first photoresist pattern; coating the semiconductor substrate comprising the partial via hole with a spin-on-glass (SOG) layer to fill the partial via hole with the SOG layer; forming a second photoresist pattern on the semiconductor substrate comprising the SOG layer is formed, wherein the second photoresist pattern comprises a second opening aligned with the partial via hole and having a second width greater than the first width; etching the SOG layer and the hard mask layer on the second interlayer insulating layer using the second photoresist pattern as an etching mask; removing the second photoresist pattern; wet-etching and removing the SOG layer formed on the hard mask layer and in the partial via hole; and forming a wiring region having the second width and a via hole in the second and first interlayer insulating layers by etching the second and first interlayer insulating layers, respectively, using the hard mask layer as an etching mask.
 41. The method of claim 40, wherein the conductive layer comprises a copper wiring layer.
 42. The method of claim 40, wherein the first stopper comprises one of a silicon nitride layer and a silicon carbide layer, having an etching selectivity to the first interlayer insulating layer.
 43. The method of claim 40, wherein the second stopper layer comprises one of a silicon nitride layer and a silicon carbide layer, having an etching selectivity to the second interlayer insulating layer.
 44. The method of claim 40, wherein the first interlayer insulating layer is formed of a material having a high etching selectivity to the first stopper layer and the hard mask layer and a low dielectric constant.
 45. The method of claim 44, wherein the first interlayer insulating layer comprises one of a SiOC layer, a porous SiO₂ layer, a phosphorous silicate glass (PSG) layer, a boron phosphorous silicate glass (BPSG) layer, an undoped silicate glass (USG) layer, a fluorine-doped silicate glass (FDSG) layer, a high-density plasma (HDP) layer, a plasma-enhanced tetraethylorthosilicate (PE-TEOS) layer, and a spin-on-glass (SOG) layer.
 46. The method of claim 40, wherein the second interlayer insulating layer is formed of a material having a high etching selectivity to the second stopper layer and the hard mask layer and a low dielectric constant.
 47. The method of claim 46, wherein the second interlayer insulating layer comprises a SiOC layer.
 48. The method of claim 40, wherein the second interlayer insulating layer is formed of the same material as the first interlayer insulating layer.
 49. The method of claim 40, wherein the hard mask layer comprises one of a silicon nitride layer and a silicon carbide layer, having a high etching selectivity to the second interlayer insulating layer and the first interlayer insulating layer.
 50. The method of claim 40, wherein the spin-on-glass (SOG) layer comprises one of a hydro silsesquioxane (HSQ) layer and a SiO₂ layer, having a high etching selectivity to the second interlayer insulating layer.
 51. The method of claim 40, wherein the wet etching of the spin-on-glass (SOG) layer is performed using a HF solution that etches only the spin-on-glass (SOG) layer.
 52. The method of claim 40, wherein the step of etching the spin-on-glass (SOG) layer and the hard mask layer on the second interlayer insulating layer using the second photoresist pattern as an etching mask is performed using an etching gas comprising one of a C_(x)F_(y)-based gas, a C_(x)H_(y)F_(z)-based gas, an inert gas, CO, CO₂ and O₂.
 53. The method of claim 40, further comprising the steps of: removing the first stopper layer exposed through the via hole; forming a barrier layer along the step difference of the semiconductor substrate; depositing a conductive material on the semiconductor substrate on which the barrier layer is formed and filling the wiring region and the via hole with the conductive material; and performing chemical mechanical polishing on the semiconductor substrate.
 54. The method of claim 40, wherein the barrier layer comprises one of a Ta layer, a TaN layer, a Ti layer, a TiN layer, and a combination thereof. 